Laser induced fluorescence Spectroscopy

The performance of optical coatings for high power DUV/VUV laser applications depends amongst others on residual absorption in the thin film layers due to impurities or defects.

We demonstrate the high potential of the laser induced fluorescence for detecting particular absorbing species even within the small interaction volume of optical thin films. Using pulsed ArF laser induced fluorescence measurements (LIF), characteristic non-intrinsic emissions of praseodymium, cerium and hydrocarbons are identified in fluoridic single layers on silicon substrates and high reflecting mirrors on CaF2 substrates. For praseodymium, additional direct and absolute absorption measurements using IPHT’s LID technique (laser induced deflection) show the influence of different impurity content on the absorption of high reflecting mirrors.

Figure 1: Fluorescence spectrum of a LaF3 single layer (thickness: 50 nm) after excitation with an ArF laser at 193 nm

For investigating laser induced fluorescence in optical thin films upon pulsed ArF laser excitation (l=193 nm) a setup is applied consisting of the following components:

  • ArF-Laser COMPEX (Coherent)
  • Imaging spectrograph Shamrock SR-303i-B using gratings 150 l/mm and 1200 l/mm
  • Andor iStar ICCD detector DH740i-18F-03 with controller
  • Optical fiber coupling
  • Particular interference filters to block scattered ArF laser light

Laser induced fluorescence measurements (LIF) are a common way to sensitively detect small traces of defects or impurities in several media such as bulk materials, liquids or gases. In the thin film community, however, LIF measurements are only rarely used so far for investigations. This is possible due to the very small interaction volume between the excitation laser and the thin film and therefore the expected very weak fluorescence signal. On the other hand, defect densities in thin films due to the manufacturing process are expected to be larger than for the corresponding bulk material.

Figure 2a): Comparison of the praseodymium fluorescence at 250 and 270 nm for several high reflecting (HR) mirrors for 193 nm applications and

Figure 1 shows the ArF laser excited LIF spectrum (H=15 mJ/cm2, f=10 Hz) for a single LaF3 layer of only 50 nm thickness deposited onto a silicon wafer. The silicon wafer as substrate material is chosen since it has been demonstrated that silicon shows no fluorescence upon 193 nm excitation. Therefore, all detected fluorescence originates from the deposited thin film. The spectrum is taken using a recording duration of 10 µs. The LIF spectrum consists of two sharp peaks at 250 nm and 270 nm, a double peak between 280 nm and 310 nm and a broad peak around 430 nm with a small peak at 400 nm. From reported data in the literature the observed emissions are presumably due to traces of trivalent praseodymium (250 nm, 270 nm and 400 nm), trivalent cerium (285 nm and 305 nm) and hydrocarbons (430 nm).

One main goal of LIF investigations is to correlate the directly measured absorption data to particular defects or impurities in order to get a better understanding of the residual absorption within optical coatings. Figure 2a shows the LIF spectra of several high reflecting (HR) coatings (designed for 193 nm applications, combination of LaF3 and MgF2) in the wavelength range 240…280 nm indicating different quantities of praseodymium. For these comparative measurements the recording duration for the spectra is 1 µs taking into account the fluorescence lifetime of the praseodymium emission.

Figure 2b) directly measured absorption of the HR mirrors as a function of the praseodymium content (in arbitrary units) taken from the LIF measurements

Figure 2b shows the absorption data obtained for the different HR coatings as a function of the praseodymium content (in arbitrary units). Except from one sample (M6), having additionally a very dominant Ce3+ fluorescence, there is a reasonable good correlation between the Pr3+ fluorescence intensity and the measured absorption. As a conclusion, residual amounts of praseodymium are one factor that needs to be considered when optimizing the absorption in HR coatings for 193 nm applications.


Dr. Christian Mühlig
Institute of Photonic Technology e.V.
Albert-Einstein-Str. 9
07745 Jena

Phone: +49-3641-206433
Fax: +49-3641-206499

Date: N/A

Author: Andor

Category: Case Study


Download as pdf


Related assets

No Related Assets

2011 - Measurement and autocorrelation analysis of two dimensional light scattering patterns from living cells for label free classification (Matthew J. Berg, ... )
2010 - Electrochemical and spectroscopic investigations of Tb(III) in molten LiCl–KCl eutectic at high temperature (Dong Hyoung Leea,... )
2010 - Effect of Pressure on Absorption Spectra of Lycopene in n-Hexane and CS2 Solvents (Liu Wei-Long, Zhe... )
2010 - Laser-induced fluorescence and dispersed fluorescence studies of the donor–acceptor system 4-amino 3-methyl benzoic acid methyl ester and its solvated clusters: Evidence of excited-state charge-transfer reaction (Katia Le Barbu-De... )
2010 - Integrated Microfluidic System for Rapid Forensic DNA Analysis: Sample Collection to DNA Profile (Cedric Hurth, Jia... )
2010 - Required Spectral Resolution for Bioaerosol Detection Algorithms Using Standoff Laser-Induced Fluorescence Measurements (Rustad G., Kasen,... )
2010 - Laser Based Stand-Off Detection of Biological Agents ()
2010 - IR laser desorption of oligonucleotides (C. A. Hunniford, ... )
2010 - CH spectroscopic observables in He–CH4 and N2–CH4 atmospheric pressure dielectric barrier discharges (P. F. Ambrico, S.... )
2010 - Chemical Speciation of Trivalent Actinides and Lanthanides in Biological Fluids: The Dominant in Vitro Binding Form of Curium (III) and Europium (III) in Human Urine (Astrid Barkleit, ... )
2008 - Formation of gas phase macromolecular targets by laser desorption from surfaces (T. L. Merrigan )
- Multispectral LIF imaging techniquest for nondestructive assessment food quality (M.S. Kim )
- Photoluminescence of hexagonal boron nitride (Luc Museur)
- Reconstructed 3D Flame Structures in Noise-Controlled Swirl-Stabilized Combustor (M Tanahashi )
- laser vaporization of mercury (L. Philippet)